Effect of irradiation on grain size and texture in Mo and Ta films

Мұқаба

Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

Implantation of heavy ions into metal matrices leads to the creation of a high concentration of radiation defects. X-ray diffraction studies of Mo and Ta foils implanted with 57Fe ions have been carried out. It is shown that the implantation of Fe ions does not significantly affect the lattice parameters. It has been established that irradiation leads to broadening of diffraction lines and a decrease in the size of crystal grains. The Mo and Ta foils with {100} orientation are found to be highly textured. Irradiation with Fe ions has no noticeable effect on the texture. However, subsequent annealing at a temperature of 700°С weakens the texture on the irradiated side for Mo and Ta foils without affecting the texture of the nonirradiated side.

Толық мәтін

Рұқсат жабық

Авторлар туралы

V. Andrianov

Lomonosov Moscow State University, Skobeltsyn Institute of Nuclear Physics

Хат алмасуға жауапты Автор.
Email: andrva22@mail.ru
Ресей, 119991, Moscow

K. Bedelbekova

Institute of Nuclear Physics

Email: andrva22@mail.ru
Қазақстан, 050032, Almaty

Әдебиет тізімі

  1. Григорьев Е.Г., Перлович Ю.А., Соловьев Г.И., Удовский А.Л., Якушин В.Л. Физическое материаловедение. Т. 4. Физические основы прочности. Радиационная физика твердого тела. Компьютерное моделирование / Ред. Калин Б.А. М.: МИФИ, 2008. 696 с.
  2. Вас Г.С. Основы радиационного материаловедения. Металлы и сплавы. М.: Техносфера, 2014. 992 с.
  3. Андрианов В.А., Бедельбекова К.А., Озерной А.Н., Верещак М.Ф., Манакова И.А., Дектерева А.С. // Поверхность. Рентген., синхротр. и нейтрон. исслед. 2020. № 4. С. 63. https://doi.org./10.31857/S1028096020040032
  4. Andrianov V.A., Bedelbekova K.A., Trigub A.L. // Vacuum. 2021. V. 193. Р. 110521. https://doi.org/10.1016/J.Vacuum.2021.110521
  5. Андрианов В.А., Бедельбекова К.А., Ерзинкян А.Л., Тригуб А.Л. // Поверхность. Рентген., синхротр. и нейтрон. исслед. 2022. № 7. С. 3. https://doi.org./10.31857/S1028096022070020
  6. Program SRIM. http://www.srim.org/
  7. Downey M.E., Eyre B.L. // Philosoph. Mag. 1965. V. 11. № 109. P. 53. http://doi.org./10.1080/14786436508211924/
  8. Лобанов М.Л., Юровских А.С., Кардонина Н.И., Русаков Г.М. Методы исследования текстур в материалах. Екатеринбург: Изд-во Урал. ун-та, 2014. 115 с.
  9. Уманский Я.С., Скаков Ю.А., Иванов А.Н., Расторгуев Л.Н. Кристаллография, рентгенография и электронная микроскопия. М.: Металлургия, 1982. С. 584.
  10. Scherrer P. // Göttinger Nachrichten Gesell. 1918. V. 2. P. 98.
  11. Patterson A. // Phys. Rev. 1939. V. 56. № 10. P. 978. https://doi.org./10.1103/PhysRev.56.978
  12. Чижов П., Левин Э., Митяев А., Тимофеев А. Приборы и методы рентгеновской и электронной дифракции. Учебное пособие. М.: Московский физико-технический институт, 2011. 151 c.

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML
Жүктеу
2. Fig. 1. Concentration depending on depth: a – implanted 57Fe atoms in the Mo (1) and Ta (2) matrices; b – primary defects for Mo (1) and Ta (2). Calculations were performed using the SRIM-2013 program; displacement energy Ed(Mo) = 60 eV and Ed(Ta) = 90 eV.

Жүктеу (226KB)
Метадеректер
3. Fig. 2. Diffractogram of Mo and Ta foils implanted with 57Fe ions. Changes from the irradiated (Irr) and reversed sides (Back): a – Ta-Irr; B – Ta-Back; c – Mo-Irr; d – Mo-Back.

Жүктеу (322KB)
Метадеректер
4. 3. The intensity of X–ray reflexes 110, 100, 211 and 220 in textured foils Mo (a) and Ta (b):

Жүктеу (190KB)
Метадеректер

© Russian Academy of Sciences, 2024