Superhydrophobisation of Painted Surfaces to Improve Their Protective Properties and Impart New Functional Properties to Materials

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅或者付费存取

详细

The method of superhydrophobization of the epoxy enamel layer based on the use of pulsed laser treatment and chemisorption of fluorinated silane on the textured enamel surface is proposed. It is shown that flexible control of laser irradiation parameters makes it possible to texture the enamel surface without overheating and subsequent destruction. Experimental studies have shown that the proposed superhydrophobic treatment can significantly improve the protective properties of enamel and impart it new functional properties, such as water-repellent properties with extreme contact and roll-off angles, increased resistance to both abrasive loads and surface stresses arising in the three-phase contact zone during water crystallization and ice melting.

全文:

受限制的访问

作者简介

E. Kuzina

Frumkin Institute of Physical Chemistry and Electrochemistry, Russian Academy of Sciences

Email: ame@phyche.ac.ru
俄罗斯联邦, 119071 Moscow

A. Emelyanenko

Frumkin Institute of Physical Chemistry and Electrochemistry, Russian Academy of Sciences

编辑信件的主要联系方式.
Email: ame@phyche.ac.ru
俄罗斯联邦, 119071 Moscow

L. Boinovich

Frumkin Institute of Physical Chemistry and Electrochemistry, Russian Academy of Sciences

Email: ame@phyche.ac.ru

Academician of the RAS

俄罗斯联邦, 119071 Moscow

参考

  1. Бойнович Л.Б. // Вестник РАН. 2013. Т. 83. № 1. С. 10–22. https://doi.org/10.7868/S0869587313010039
  2. Ogihara H., Okagaki J., Saji T. // Langmuir. 2011. V. 27. № 15. P. 9069–9072. https://doi.org/10.1021/la200898z
  3. Manabe K., Saikawa M., Sato I., Loo C.S., Takashima K., Norikane Y. // ACS Appl. Polym. Mater. 2024. V. 6. № 22. P. 13701–13709. https://doi.org/10.1021/acsapm.4c02416
  4. Бузник В.М. // Авиационные материалы и технологии. 2013. № 1 (26). С. 29–34.
  5. Бойнович Л.Б., Бузник В.М., Гракович П.Н., Грязнов В.И., Пашинин А.С., Юрков Г.Ю. // Докл. АН. 2015. Т. 462. № 4. С. 431–434. https://doi.org/10.7868/S0869565215160124
  6. Кондрашов Э.К., Нефедов Н.И., Веренинова Н.П., Кущ П.П., Кичигина Г.А., Кирюхин Д.П., Бузник В.М. // Все материалы. Энциклопедический справочник. 2016. № 1. С. 2–10.
  7. Кузина Е.А., Емельяненко К.А., Домантовский А.Г., Емельяненко А. М., Бойнович Л.Б. // Коллоид. журн. 2022. Т. 84. № 4. С. 453–464. https://doi.org/10.31857/S0023291222040097
  8. Diker C.Ö., Duman O., Tunç S. // Appl. Clay Sci. 2023. V. 244. P. 107109. https://doi.org/10.1016/j.clay.2023.107109
  9. Diker C.Ö., Duman O., Tunç S. // Appl. Clay Sci. 2024. V. 262. P. 107626. https://doi.org/10.1016/j.clay.2024.107626
  10. Емельяненко А.М., Бойнович Л.Б. // Приборы и техника эксперимента. 2002. Т. 45. С. 52–57.
  11. Кузина Е.А., Омран Ф.Ш., Емельяненко A.М., Бойнович Л.Б. // Коллоид. журн. 2023. Т. 85. № 1. С. 63–70. https://doi.org/10.31857/S0023291222600614
  12. Залесский Б.В., Флоренский К.П. // Труды института геологических наук. АН СССР. 1952. Т. 146. № 42. С. 39–50.
  13. Wenzel R.N. // Ind. Eng. Chem. 1936. V. 287 № 8. P. 988–994. https://doi.org/10.1021/ie50320a024
  14. Prorokova N.P., Vavilova S.Y., Bouznik V.M. // J. Fluorine Chem. 2017. V. 204. P. 50–58. https://doi.org/10.1016/j.jfluchem.2017.10.009
  15. Севостьянов Н.В., Розен А.Е., Бузник В.М., Логинов О.Н., Усатый С.Г., Болсуновская Т.А. // Трение и износ. 2020. Т. 41. № 1. С. 55–62.
  16. Севостьянов Н.В., Бурковская Н.П., Бузник В.М. // Трение и износ. 2015. Т. 36. № 6. С. 671–674.
  17. Stern M., Geary A.L. // J. Electrochem. Soc. 1957. V. 104. P. 56–63. https://doi.org/10.1149/1.2428496
  18. Bäuerle D. Material transformations, laser cleaning. In: Laser processing and chemistry. Berlin, Heidelberg: Springer, 2011. P. 535–559. https://doi.org/10.1007/978-3-642-17613-5_23

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. Three-dimensional images of the surface profile of superhydrophobized paint obtained by confocal microscopy before (a) and after (b) 120 minutes of abrasive exposure under a layer of vibrating sand.

下载 (181KB)
索引源数据
3. Fig. 2. Changes in the angles of wetting (1, 2) and rolling (3, 4) for the surface of two superhydrophobic samples under the influence of cycles of water crystallization/ice melting.

下载 (41KB)
索引源数据
4. Fig. 3. The change in the angles of wetting (1, 2) and rolling (3, 4) for the surface of two superhydrophobic samples, as well as the angle of wetting for the surface of the painted sample without subsequent treatment (5), depending on the time of abrasive action on the samples. The droplet images on curves (1, 2) correspond to sitting droplets before the abrasive load (on the left) and after 120 minutes of abrasive action (on the right). The inset shows the change in the mass of colored samples after laser treatment (2) and without treatment (5) as a result of abrasive action.

下载 (58KB)
索引源数据
5. Fig. 4. Changes in the electrochemical characteristics of a sample of D16 alloy with initial (1.1ʹ) and superhydrophobic (2.2ʹ, 2ʹʹ) colorful layers of EP-140 enamel during prolonged contact with 0.5 M NaCl solution: (a) evolution of the corrosion current (1, 2) and polarization resistance (1.2ʹ) of the coating(b) frequency dependences of the impedance modulus for different contact times: 24 hours (1, 2); 42 days (1, 2); 60 days (2).

下载 (72KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2024